Building Material – Bricks ! Brick Type of Perforations or Cavities :

Three Following Types of Perforation or Cavities Bricks :

Perforated bricks
Hollow bricks
Channeled bricks

Perforated Bricks :

These form a modern class of building bricks.

In perforated bricks cylindrical, rounded or rectangular holes are made in the bricks after the moulding stage. These holes are called perforations.

They are properly spaced from the side of the brick, minimum distance being 15mm. further, distance between any two perforations is not less than 10mm the volume of the perforations. May be as much as 20-50 percent of the total volume of the brick.

Advantages :

These bricks are light in weight.

Less quantity of clay is required for their manufacture;

Less time is required for drying and burning of perforated bricks.

These offer better resistance against rain penetration and better insulation against heat. As such they are ideally suited for tropical countries.
Efflorescence is least in perforated bricks.
These are specially suitable for construction of brick panels in- multi-storeyed structures.

Hollow Bricks :

A brick also called cavity brick or cellular brick has a few well- defined sets of cavities with specified dimensions made in the body of the brick.

Its net weight may be only one- third to one- half of the solid brick. It is important that the thickness of brick wall near the cavity should not be less than 2 cm. Hence cavity extends throughout the body of the brick.

The hollow bricks are made from special type of brick clay (which should have higher clay content).

Advantages :

Being light in weight, they can be handled more conveniently and the output of the mason may be three to four times compared with ordinary bricks.
They offer better insulation against heat and sound.
They are ideal and economical for non- load bearing walls, e.g in partition walls.

Channel or Gutter Bricks :

They are actually special purpose bricks having a continuous central semicircular cavity or depression running through their length very often they are glazed to make them impervious.

These find use in the laying of drains.

https://www.facebook.com/ArchitectureInteriorDesignStudio/

Building Material _ Bricks ! Shapes of Bricks ! Part 2

SHAPES OF BRICKS :

King Closer : the brick is so cut that it has length and width on one side only.Uses splayed jambs,blunt corners of walls.

Queen Closer : it is also a cut brick. The cut is lengthwise so that brick has only one half of the length of the full bricks. Uses bonding of brick works.

Squint Brick : it is also cut brick.the portion of cut forms angles other than right angle. Uses exterior or interior corners are to be built at some angle and also for ornamental purposes.

Splay Bricks or cant bricks : these have a level or portion taken off, widthwise, lengthwise, or in both directions. Uses for pillars , on top course of plith,on exterior walls etc.
Plinth Header : it has a full length on one face. On the other face, a slope (bevel) is made from 3/4^th of the length (D)

Plinth Stretcher : it has slope from one half of the width that extends along the entire length (E).
Plinth Return : it is a combination of both the header and stretcher beveling (F).

Coping Bricks : when a coping is to be provided to a wall, a special shape may be desired. The chamfered brick, the half round brick and the saddle back brick are some common coping bricks.

Bull Nose : it is otherwise a standard brick having one arris or edge rounded. Uses for decoration purposes.

Cow Nose : it is similar to a bull nose but has both edges on the side rounded. It may be called a double bullnose. Use for ornamental purpose.

Miscellaneous Shapes : these include bricks shaped for very specific purpose (not covered above) as for arches and circular walls, chimneys and culvets and wells.

https://www.facebook.com/ArchitectureInteriorDesignStudio/

Building Material – Brick & Bricks Classification

Classification of Bricks :

Conventionally , the Bricks are classified in the following two types :

Sun dried or Katcha Bricks :
Burnt or Pucca bricks :

Sun Dried or Katcha bricks :

The bricks dried only in the sun after their moulding are called sun dried or Katcha Bricks.These should not be used at places exposed to heavy rains.

Uses : These are suitable for constructing temporary houses,enclosures etc. in rural area.

Burnt or Pucca Bricks :

These brick burnt in a clamp or klin,after moulding and drying are called burnt or pucca bricks.

These are hard,strong and durable.

Uses : These are generally in permanent works.

These further classified into the following four types :

FIRST CLASS BRICKS :

CHARACTERISTICS :

(i) Well burnt having even surface , perfectly rectangular shape & free from saline deposits.

(ii) When two bricks are struck against each other a ringing- sound is produced.

(iii) Its compressive strength shall not be less than 140kg/cm2 and its absorption after 24 hours, immersion shall not exceed 20 percent.

(iv) It should show a uniform appearance,colour , texture and structure when seen on fracturing.

(v) They shall be clean,smooth & free from cracks,chips,grits,holes , nodules of lime or kankar etc.

(vi) They shall not show any sign of efforescence on surface when dried in the shade.

(vii) They shall not absorb water more than 20% by weight after 24 hours immersion in cold water.

(viii) They shall have a minimum crushing strength of 105kg/sq.cm.

Uses : Every kind of masonry work, flooring etc. Where strength and durability is desired. They are also used for face work,reinforced brick work and as ballast for base concrete work in floors.

SECOND CLASS BRICKS :

CHARACTERISTICS :

Well burnt, even slight over burning is accepted.
Metallic-ringing sound is also a must in this case as well.
In shape, rectangular, but slight irregularity is permitted. Surface may be slightly uneven.
Compressive strength shall not be less than 70kg/cm2 and absorption value between 20-22 percent.
Slight difference in structure on fractured surface is admissible.
They have fine , compact ,uniform texture.
They may have slightly chips , flaws or surface cracks but shall be free from lime & kankar nodules.
They are not so hard & strong.
They shall have a minimum crushing strength of 70 kg/sq.cm.
They shall not absorb water more than 22% by weight after 24 hours immersion in cold water.
They shall not show any sign of efflorescence on surface either in wet or in dry state.

Uses : These used in unimportant situations where bricks are hidden from front views as in the case of interior walls. They are never used in reinforcement brick work or face works of building.

THIRD CLASS BRICKS :

CHARACTERISTICS :

Poorly and unevenly burnt, that is, may be over burnt or under burnt.
On striking a dull thud (rather than metallic sound) is produce.
Appearance, shape and size are also non- uniform and irregular.
Compressive strength lies between 35- 70 kg/cm2 and absorption between 22-25 percent.
Yellowish in colour & may be distorted and have round edges.
They are soft & weak in strength.
They shall not absorb water more than 25% by weight after 24 hours immersion in cold water.

Uses : These used in inferior and temporary buildings & in place not subjected to heavy rains . They are sometimes used for scaffolding and centring in the construction of building.

JHAMA OR FOURTH CLASS / OVER BURNT BRICKS :

CHARACTERISTICS :

Irregular in shape and dark in colour, which is due to over burning.
Quite strong in compressive strength, generally above 150kg/cm2 and low in porosity and absorption.
They shall be over burnt , vitrified & distorted bricks.
They shall be dark in colour.
They shall be irregular in shape & size and may be available in the form of lumps.
They shall be hard & strong.
Produce metallic sound when struck with one another.

Uses : They are used as aggregates for making base for concrete to be used in foundations, floors etc. and as road metal for soling coats.